標題: | Gallium nitride microcavities formed by photoenhanced wet oxidation | 作者: | LUNG-HAN PENG Lu, C.-Y. Wu, W.-H. Wang, S.-L. |
公開日期: | 2005 | 卷: | 87 | 期: | 16 | 起(迄)頁: | 1-3 | 來源出版物: | Applied Physics Letters | 摘要: | We report the formation of gallium nitride (GaN) microcavities by manipulating a photoenhanced oxidation rate difference between the polar and nonpolar crystallographic planes of GaN. When immersed in a buffered acetic (C H3 COOH) electrolyte of pH∼6.2 at room temperature, it is shown that the photo-oxidation can proceed at a rate that is one order of magnitude slower on the nonpolar plane of {1 1- 00}GaN than on the polar plane of {000 1- }GaN due to the reduced surface field action. Gallium nitride microcavities bounded by optically smooth {1 1- 00} and {1 1- 03} facets can thus be preferentially formed on the c -plane sapphire substrate after dissolving the oxide layer. The optical properties of these GaN hexagonal cavities reveal characteristic peaks of whispering gallery modes in resonance with the GaN band edge emission spectrum. A typical cavity Q factor of 103 is observed in these GaN microcavities due to a reduced optical scattering loss in the wet chemical reaction process. © 2005 American Institute of Physics. |
URI: | http://ntur.lib.ntu.edu.tw//handle/246246/146017 https://www.scopus.com/inward/record.uri?eid=2-s2.0-28344449716&doi=10.1063%2f1.2103423&partnerID=40&md5=8b6c8237ff7b966855cc095f40de9470 |
ISSN: | 00036951 | DOI: | 10.1063/1.2103423 | SDG/關鍵字: | Electrolytes; Oxidation; pH effects; Sapphire; Band edge emission; Microcavities; Photoenhanced oxidation; Gallium nitride |
顯示於: | 電機工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。