標題: | Infrared studies of laser induced oxide on (1 0 0) Si and SiGe layers | 作者: | CHEE-WEE LIU Huang, Y.S. Chen, C.Y. Gurtler, S. CHIH-CHUNG YANG Chang, Y. Chen, L.P. |
公開日期: | 2000 | 卷: | 65 | 期: | 3 | 起(迄)頁: | 350-353 | 來源出版物: | Materials Chemistry and Physics | 摘要: | Oxide layers have been grown on single crystal (1 0 0) Si and SiGe surfaces with exposure to a pulsed UV laser at 266 nm under various controlled environments. During the growth, sample surfaces were first melted by the laser power. Oxygen related species then diffused into the melt. Oxide was formed after the samples re-solidified. Besides the strong stretching mode absorption at 1080 cm-1 (T2 mode), there was an intense shoulder around 1200 cm-1 (the A1 mode) in the Fourier transform infrared spectrum, compared to thermal oxide. The relative intensity of the shoulder decreased with ambient water vapor concentration. The porosity of this oxide leads to the intense shoulder and more water vapor incorporation can decrease the porosity. The porous oxide could be annealed to some extent with a high-temperature thermal process. Because the adsorption and diffusion of water molecules to and in melted silicon are easier than oxygen molecules, ambient water vapor can fill the voids in the oxide more efficiently and leads to less significant absorption shoulder than oxygen molecules. Also because the diffusion of water molecules in Ge is faster than in Si, less voids are formed and hence the absorption shoulder is less prominent in SiGe samples. |
URI: | http://www.scopus.com/inward/record.url?eid=2-s2.0-0033701976&partnerID=MN8TOARS http://scholars.lib.ntu.edu.tw/handle/123456789/289106 https://www.scopus.com/inward/record.uri?eid=2-s2.0-0033701976&doi=10.1016%2fS0254-0584%2800%2900252-2&partnerID=40&md5=6891e866876d8c26e3911d1f297d9261 |
ISSN: | 02540584 | DOI: | 10.1016/S0254-0584(00)00252-2 | SDG/關鍵字: | Adsorption; Diffusion in solids; Fourier transform infrared spectroscopy; Laser applications; Laser beam effects; Porosity; Porous materials; Semiconducting silicon; Semiconducting silicon compounds; Silica; Single crystals; Thermooxidation; Laser induced oxides; Silicon germanide; Ultrathin films |
顯示於: | 電機工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。