標題: | Preparation and mechanism of nest-like YBO3:Tb3+ phosphors synthesized via the microemulsion-mediated hydrothermal process | 作者: | Chung C.-Y. Hsu C.-H. Lu C.-H. |
公開日期: | 2011 | 卷: | 94 | 期: | 9 | 起(迄)頁: | 2884-2889 | 來源出版物: | Journal of the American Ceramic Society | 摘要: | YBO3:Tb3+ phosphors with nest-like and apple-like morphology were synthesized via the microemulsion-mediated hydrothermal process at a reaction temperature as low as 180¢XC. This process significantly reduced the reaction duration and temperatures as compared with the conventional processes. The YBO3:Tb3+ powders prepared via the microemulsion-mediated hydrothermal process had smaller particle sizes in comparison with the hydrothermal process. In the growth process, the nanoflakes assembled to spheres in revolved order. Each nanoflake protruded out of the spheres, followed by transforming into completed multilayers to form the nest-like particles. When the prepared phosphors were excited with the wavelength of 240 nm, the emission peaks in the range from 487 to 628 nm are related to the transitions from 5D4 to 7F J (J=3-6) levels of Tb3+ ions. As the reaction temperatures were increased, the lifetimes were increased due to decrease in the defect centers. The reduced defect centers and enhanced crystallinity of the prepared samples cause the luminescent intensity to increase. ? 2011 The American Ceramic Society. |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/407409 | ISSN: | 00027820 | DOI: | 10.1111/j.1551-2916.2011.04466.x |
顯示於: | 化學工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。