標題: | Effects of structural crystallinity and defects in microporous Al-MOF filled chitosan mixed matrix membranes for pervaporation of water/ethanol mixtures | 作者: | Vinu M. Senthil Raja D. Jiang Y.-C. Liu T.-Y. Xie Y.-Y. Lin Y.-F. Yang C.-C. Lin C.-H. Alshehri S.M. Ahamad T. Salunkhe R.R. Yamauchi Y. Deng Y.-H. Wu K.C.-W. |
關鍵字: | Chitosan;Metal-organic frameworks;Mixed matrix membrane;Pervaporation process;Separation | 公開日期: | 2018 | 卷: | 83 | 起(迄)頁: | 143-151 | 來源出版物: | Journal of the Taiwan Institute of Chemical Engineers | 摘要: | A new two-dimensional microporous metal organic framework (MOF), Al-MOF, [Al(OH)(MBA)] (CYCU-7, MBA = diphenylmethane-4,4¡¬-dicarboxylate anion) and its reported analogue, [Al(OH)(SBA)] (CAU-11, SBA = 4,4¡¬-sulfonyldibenzoate anion), have been synthesized using hydrothermal and solvothermal methods, respectively, and their structural crystallinities and defect porosities were carefully controlled and characterized by N 2 sorption isotherms and 27 Al solid-state nuclear magnetic resonance measurements. Interestingly, the MOF synthesized by the ethanol-based solvothermal method (CYCU-7) show a significant degree of linker-missing defects compared to that synthesized by the water-based hydrothermal method (CAU-11). We further incorporated the synthesized CYCU-7 and CAU-11 with chitosan (CS) biopolymer to make CYCU-7@CS and CAU-11@CS mixed matrix membranes (MMMs) with the loading amount of MOF 2.5, 5.0, or 10 wt%. The as-prepared CYCU-7@CS and CAU-11@CS MMMs were applied for separation of water/ethanol mixtures through the pervaporation process, and the effects of the structural properties (e.g. crystallinity and defects) of CYCU-7 and CAU-11 on the separation performance are studied. It is found that defect-rich CYCU-7@CS MMMs exhibit higher flux, while CAU-11@CS MMMs with higher crystallinity exhibit a higher separation factor. In addition, the CAU-11@CS MMM with 5.0 wt% loading of CAU-11 displays the best separation performance (separation factor = 2741 and flux = 458 g/m 2 h). ? 2017 Taiwan Institute of Chemical Engineers |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/408879 | ISSN: | 18761070 | DOI: | 10.1016/j.jtice.2017.11.007 |
顯示於: | 化學工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。