標題: | Harnessing the interplay of Fe–Ni atom pairs embedded in nitrogen-doped carbon for bifunctional oxygen electrocatalysis | 作者: | Zhu X Zhang D CHIH-JUNG CHEN Zhang Q Liu R.-S Xia Z Dai L Amal R Lu X. RU-SHI LIU |
關鍵字: | Atoms; Benchmarking; Binding energy; Binding sites; Carbon; Catalysts; Cost effectiveness; Doping (additives); Durability; Electrocatalysis; Electrolytic reduction; Electronic structure; Iridium compounds; Iron; Nitrogen; Oxygen; Oxygen reduction reaction; Platinum compounds; Precious metals; Reaction intermediates; Reaction kinetics; Ruthenium compounds; Tuning; Zinc air batteries; Charge-discharge cycling test; Dual metals; Large-scale applications; Nitrogen-doped carbons; Oxygen evolution reaction (oer); Performance degradation; Rechargeable zinc-air batteries; Theoretical calculations; Oxygen evolution reaction | 公開日期: | 2020 | 卷: | 71 | 來源出版物: | Nano Energy | 摘要: | Oxygen evolution reaction (OER) and oxygen reduction reaction (ORR) both have sluggish kinetics, which normally requires the use of noble metal-based catalysts (e.g. RuO2, IrOx and Pt). Unfortunately, the high cost of these noble metals has severely restricted their large-scale applications. Herein, we report the fabrication of a cost-effective OER/ORR bifunctional catalyst by embedding atomic Fe–Ni dual metal pairs into nitrogen-doped carbon hollow spheres (Fe–NiNC-50). The resultant catalyst shows exceptional catalytic performance towards both OER and ORR, which is even comparable to the noble metal-based benchmarks. By virtue of its bi-functionality, a rechargeable zinc-air battery is constructed and presents high power density (~220 mW cm?2), stable discharge voltage and large specific energy density (~932.66 Wh kgZn ?1). Moreover, the rechargeable Zn-air battery exhibits long-term durability in a charge-discharge cycling test (100 h) with negligible performance degradation. The outstanding bifunctional catalytic performance can be ascribed to the formation of Fe–Ni atomic pairs, which imposes mutual effects for tuning electronic structures of both Fe and Ni sites. Experiments and theoretical calculations further unravel that the electronically modified Ni and Fe atoms are the active sites for OER and ORR, respectively, facilitating both OER and ORR by tuning the binding energy of the reaction intermediates. ? 2020 Elsevier Ltd |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-85079694990&doi=10.1016%2fj.nanoen.2020.104597&partnerID=40&md5=2ec8a5fc5a0b88cc032dc6d67d5ba735 https://scholars.lib.ntu.edu.tw/handle/123456789/575851 |
ISSN: | 22112855 | DOI: | 10.1016/j.nanoen.2020.104597 |
顯示於: | 化學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。