標題: | Robust thermoplastic polyurethane elastomers prepared from recycling polycarbonate | 作者: | Huang Y.-C Huang Y.-H Chen L.-Y Dai C.-A Dai S.A Chen Y.-H Wu C.-H CHI-AN DAI RU-JONG JENG |
關鍵字: | Ethers; Mixtures; Molecular weight; Monomers; Phase separation; Polycarbonates; Polyurethanes; Reinforced plastics; Thermoplastic elastomers; X ray scattering; Elastomeric properties; Enhanced reactivity; High molecular weight; Phenolic hydroxyl group; Polymer properties; Processing condition; Thermoplastic polyurethane elastomers; Thermoplastic polyurethanes; Recycling | 公開日期: | 2021 | 卷: | 212 | 來源出版物: | Polymer | 摘要: | Polymer properties along with recycling processes remain a constant challenge for post-recycled polymers. In this study, the development of recycling feasibility, monomers reactivity, and the chemical-recycled polymer properties from polycarbonate (PC) waste were demonstrated. Through selective aminolysis under mild conditions, the reduced molecular-weight products (or monomer mixtures) with newly incorporated flexible-ether linkages as building blocks were realized. By using the commodity monomers such as isocyanate reagents, monomer mixtures were readily to be re-connected into polyurethanes in one-pot process without prior purification of the recycled monomer mixtures. Due to the presence of urethane groups, the enhanced reactivity of the terminal phenolic hydroxyl groups of the monomer mixtures toward isocyanate groups would afford high molecular weights over ~80,000 g/mol for thermoplastic polyurethanes (TPUs). Moreover, by taking advantage of low melting point polyether-type polyols along with optimizing processing conditions, the TPUs exhibited a unique phase separation morphology with domain sizes ranging from ~10 nm to ~25 nm as investigated by using small angle X-ray scattering (SAXS) measurements. This work demonstrate that the PC waste was fully transformed into TPUs which exhibited improved elastomeric properties. ? 2020 Elsevier Ltd |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-85097721307&doi=10.1016%2fj.polymer.2020.123296&partnerID=40&md5=24e4c461411ec7be4fbad9f9db33eab1 https://scholars.lib.ntu.edu.tw/handle/123456789/576234 |
ISSN: | 323861 | DOI: | 10.1016/j.polymer.2020.123296 |
顯示於: | 化學工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。