標題: | Fatigue studies of CoCrFeMnNi high entropy alloy films using nanoindentation dynamic mechanical analyses | 作者: | Wang Z Wang C Zhao Y.-L Kai J.-J Liu C.-T Hsueh C.-H. CHUN-HWAY HSUEH |
關鍵字: | Chromium alloys; Cobalt alloys; Dynamics; Electromechanical devices; Entropy; Fatigue testing; High-entropy alloys; Iron alloys; Manganese alloys; MEMS; Metallic films; Nanoindentation; Bulk counterpart; Dynamic mechanical analysis (DMA); Fatigue lifetime; Fatigue loadings; Fatigue properties; Fatigue strength; Grain size; Loading cycles; Fatigue of materials | 公開日期: | 2021 | 卷: | 410 | 來源出版物: | Surface and Coatings Technology | 摘要: | Films in the microelectromechanical systems are frequently subjected to the fatigue damage under cyclic loading, and the fatigue properties of the films greatly influence the reliability and life of MEMS. However, because of the small dimension of films, characterization of their fatigue properties is a daunting challenge. Nanoindentation dynamic mechanical analysis (DMA) provides a possible solution. However, the setting of loading cycles is crucial to the fatigue test. Using CoCrFeMnNi high entropy alloy films, we investigated the fatigue properties extracted using two different types of loading: fixed load ratio with different mean loads and fixed mean load with different load ratios. Our results showed that both types of fatigue loading were reliable for the evaluation of the fatigue properties of films and it was demonstrated by the fatigue strength coefficients and exponents extracted from the test results. For comparison, DMA was also performed on CoCrFeMnNi high entropy alloys. Compared to the bulk counterpart, the film had much higher fatigue lifetime because of the thickness confinement, the presence of high-density nanotwins and the much smaller grain size in the film. ? 2021 Elsevier B.V. |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-85100681849&doi=10.1016%2fj.surfcoat.2021.126927&partnerID=40&md5=836ce6eedb44a9ebe808c96e087ffa54 https://scholars.lib.ntu.edu.tw/handle/123456789/576903 |
ISSN: | 2578972 | DOI: | 10.1016/j.surfcoat.2021.126927 |
顯示於: | 材料科學與工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。