https://scholars.lib.ntu.edu.tw/handle/123456789/576922
標題: | Highly crystalline colloidal nickel oxide hole transport layer for low-temperature processable perovskite solar cell | 作者: | HUNG-WEI YEN YULIA GALAGAN |
關鍵字: | Conversion efficiency; Emulsification; Micelles; Nanoparticles; Nickel oxide; Particle size; Perovskite; Precipitation (chemical); Sols; Synthesis (chemical); Temperature; Annealing temperatures; Chemical precipitation method; Controlled particle sizes; Hole transport layers; Large scale productions; Low-temperature deposition; Power conversion efficiencies; Tetramethyl ammonium hydroxide; Perovskite solar cells | 公開日期: | 2021 | 卷: | 412 | 來源出版物: | Chemical Engineering Journal | 摘要: | Highly crystalline NiOX usually requires high annealing temperature (>300 °C) which is incompatible with flexible substrate and might consume high amount of energy. Herein, we demonstrate a facile emulsion process to synthesize highly crystalline, low temperature deposition (<150 °C) and solution processable NiOx nanoparticles (NPs) as a hole transport layer for the perovskite solar cells (PVSCs). A novel surfactant of tetramethylammonium hydroxide (TMAOH) was used to react with Ni(NO3)2 to form Ni(OH)2 nanoparticles (NPs). The micelles of TMAOH act as a nano-reactor containing OH? anion. The Ni+ cation enters into the nano-reactor to form Ni(OH)2 NPs inside the reactor with controlled particle size. The Ni(OH)2 NPs prepared by emulsion process are further calcined to form NiOX NPs with the particle size of 8.28 ± 2.64 nm (EP-NiOX). The smaller size of EP-NiOX NPs results in a good dispersibility and an excellent stability of NPs suspension, which can be used to fabricate uniform NiOX film without any aggregates. A power conversion efficiency (PCE) of 18.85% can be achieved using this EP-NiOX film, as compared with 16.68% using the NiOX NPs synthesized from the chemical precipitation method (CPM-NiOX). Moreover, a flexible PVSCs with a PCE of 14.28% can be fabricated using the EP-NiOX film. Except for the device performance, the quality of the EP-NiOX film shows a good batch-to-batch uniformity, resulting in an excellent reproducibility of PVSCs. This work has a potential for the development of a large-scale production of PVSCs with a high energy conservation. ? 2021 Elsevier B.V. |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-85100395120&doi=10.1016%2fj.cej.2021.128746&partnerID=40&md5=1d9c25c4a9b2a725d1626b6d3648a0ca https://scholars.lib.ntu.edu.tw/handle/123456789/576922 |
ISSN: | 13858947 | DOI: | 10.1016/j.cej.2021.128746 | SDG/關鍵字: | Conversion efficiency; Emulsification; Micelles; Nanoparticles; Nickel oxide; Particle size; Perovskite; Precipitation (chemical); Sols; Synthesis (chemical); Temperature; Annealing temperatures; Chemical precipitation method; Controlled particle sizes; Hole transport layers; Large scale productions; Low-temperature deposition; Power conversion efficiencies; Tetramethyl ammonium hydroxide; Perovskite solar cells |
顯示於: | 材料科學與工程學系 |