標題: | Controlling interlayer spacing and organic solvent permeation in laminar graphene oxide membranes modified with crosslinker | 作者: | Nakagawa K Araya S Ushio K Kunimatsu M Yoshioka T Shintani T Kamio E Tung K.-L Matsuyama H. KUO-LUN TUNG |
關鍵字: | Crosslinker;Graphene oxide;Interlayer spacing;Laminar membrane;Organic solvent nanofiltration;Solvent permeation;Ketones;Nanofiltration;Nanofiltration membranes;Permeation;Triethanolamine;Cross-linkers;Graphene oxides;Interlayer spacings;Organics;Oxide membrane;Polyketones;Triethanolamines;Organic solvents | 公開日期: | 2021 | 卷: | 276 | 來源出版物: | Separation and Purification Technology | 摘要: | Two-dimensional (2D) laminar membranes are attracting much attention in organic solvent nanofiltration owing to the promising permeation and selective performance derived from their 2D ultrathin separation layer. However, owing to easy swelling (enlargement of interlayer spacing), controlling the interlayer spacing in organic solvents and stable solvent permeation are major issues for their application to organic solvent systems. In this study, laminar GO membranes were fabricated on a porous polyketone (PK) support membrane using triethanolamine (TEOA) as crosslinker (GO-TEOA/PK). The interlayer spacing (d) between GO sheets was characterized by X-ray diffraction. The TEOA crosslinker effectively suppressed swelling of the GO laminar structure. For GO-TEOA/PK, the variation in d corresponded well with the affinity between TEOA and each solvent, Ra(TEOA–solvent), as estimated using the Hansen solubility parameters. Furthermore, common linear correlation between the permeance of alcohols and the parameter combining affinity, viscosity, and equivalent molar diameter was clearly observed. Therefore, the affinity between crosslinker and solvent was an important factor in controlling interlayer spacing and solvent permeation in the laminar GO membranes containing crosslinker. ? 2021 Elsevier B.V. |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-85110357174&doi=10.1016%2fj.seppur.2021.119279&partnerID=40&md5=f43da63d1bdf516c71caa8c34f67fe6b https://scholars.lib.ntu.edu.tw/handle/123456789/598244 |
ISSN: | 13835866 | DOI: | 10.1016/j.seppur.2021.119279 |
顯示於: | 化學工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。