標題: | Heterogeneous and homogeneous nucleation of epitaxial NiSi2 in [110] Si nanowires | 作者: | Chou Y.-C.; Wu W.-W.; Lee C.-Y.; Liu C.-Y.; Chen L.-J.; Tu K.-N. YI-CHIA CHOU |
關鍵字: | [110] direction; Epitaxial silicides; Heterogeneous nucleation; High resolution; Homogeneous nucleation; In-situ observations; Incubation time; Kinetic analysis; Lattice match; Si nanowire; Step formation; TEM; TEM observations; Epitaxial growth; High resolution transmission electron microscopy; Nanowires; Silicides; Silicon; Nucleation | 公開日期: | 2011 | 卷: | 115 | 期: | 2 | 起(迄)頁: | 397-401 | 來源出版物: | Journal of Physical Chemistry C | 摘要: | We report here both heterogeneous and homogeneous nucleation of epitaxial silicide of NiSi2 in Si nanowires grown in [110] direction by in situ observation in high-resolution transmission electron microscopy (TEM). Owing to the excellent lattice match between Si and NiSi2, a giant epitaxial step of 2-8 nm wide forms at the interface between Si and NiSi2 during the growth of the latter. The step formation results in two silicide/Si interfaces parallel to each other in TEM observations. Heterogeneous nucleation of NiSi2 occurs at the intersection where the step meets the interfaces. However, we have also observed the epitaxial growth of NiSi 2 having a single interface with the Si, i.e., without a giant step. Homogeneous nucleation of NiSi2 occurs on the single interface. Incubation time of heterogeneous nucleation of NiSi2 has been measured by high-resolution video to be much shorter than that of homogeneous nucleation. The overall growth rate of NiSi2 for the case of heterogeneous nucleation is faster than that for the case of homogeneous nucleation. Kinetic analysis of both types of nucleation is presented for a direct comparison in order to have a better understanding of the nucleation events. © 2010 American Chemical Society. |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-78651465924&doi=10.1021%2fjp108686y&partnerID=40&md5=9ed8e7f9d1360ec1246a2023ee78e5c6 https://scholars.lib.ntu.edu.tw/handle/123456789/614683 |
ISSN: | 19327447 | DOI: | 10.1021/jp108686y |
顯示於: | 材料科學與工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。