Title: | A Chromate-Free and Convenient Route to Fabricate Thin and Compact Conversion Coating for Corrosion Protection on LZ91 Magnesium Alloy | Authors: | Chen C.-W Aktug S.L Chang C.-J YUEH-LIEN LEE Ger M.-D Jian S.-Y. |
Keywords: | acid pickling pretreatment; conversion coating; corrosion resistance; LZ91 magnesium alloy; microstructure | Issue Date: | 2022 | Journal Volume: | 12 | Journal Issue: | 9 | Source: | Nanomaterials | Abstract: | This study characterizes and determines the corrosion resistance of Mn-Ce conversion coated LZ91 magnesium alloy that undergoes pretreatments. It is challenging to process large and curved workpieces in the industry because the geometric shapes are complex if they are mechanically ground. This study uses acid pickling instead of mechanical grinding, and a nitric acid solution is used for pickling. After pretreatments, the samples are immersed for 30 s in a conversion coating solution containing 0.1 M KMnO4 and 0.025 M Ce(NO3)3 with a pH of 1.5, as demonstrated in previ-ous studies by the authors. The microstructure of the coating layer and electrochemical behavior of conversion coated samples exposed to 3.5 wt.% NaCl solution are studied. The corrosion behavior of Mn-Ce conversion coating specimens is determined using a salt spray test (SST). Scanning electron mi-croscopy (SEM), energy dispersive X-ray spectrometry (EDS), and X-ray photoelectron spectroscopy (XPS) are used to analyze the interface between the coating layer and the underlying magnesium substrate and to investigate the microstructure of the specimens. The roughness of the coatings is measured using 3D white light interferometry. The results show that the deteriorated area ratio for conversion coated LZ91 decreases to less than 5% after 72 h of SST exposure, and the corrosion resistance is improved 2.25 times with the Mn-Ce conversion coating on LZ91 magnesium alloy. © 2022 by the authors. Licensee MDPI, Basel, Switzerland. |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-85129679502&doi=10.3390%2fnano12091614&partnerID=40&md5=455babaa9b2fadc1b0fbcb242231e7e3 https://scholars.lib.ntu.edu.tw/handle/123456789/625111 |
ISSN: | 20794991 | DOI: | 10.3390/nano12091614 |
Appears in Collections: | 工程科學及海洋工程學系 |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.