標題: | Terminal Reaction Behaviors in Micro Bumps: Comparison of Ti and Cr Adhesion Layers | 作者: | Kao, Chen Wei Kung, Po Yu Chang, Chih Chia C. ROBERT KAO |
關鍵字: | Adhesion layer | Intermetallic | Micro bumps | Solid-state reaction | 公開日期: | 1-一月-2022 | 來源出版物: | 2022 International Conference on Electronics Packaging, ICEP 2022 | 摘要: | In this research, the terminal reaction of the Ti adhesion layer with Sn/Cu IMCs is discussed through thermal aging, which Ti is fully attached to Sn/Cu IMCs. The samples are first fabricated by electroplating Cu and Sn sequentially on the Ti adhesion layer to form micro bumps and then underwent thermal aging at 200 °C to observe the evolution between layers. After thermal aging from 0 h to 72 h, the micro bumps all transform into intermetallic structures (IMCs), yet they all attach well with the Ti adhesion layer. Moreover, the difference in diffusion rate between Cu and Sn will lead to some voids during aging. These voids will progress to the center of the bump through the depletion of the Cu layer, but they do not affect the attachment between the IMCs and the adhesion layer. To conclude, using Ti as an adhesion layer shows better adhesive behavior with IMCs than using Cr. |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/632796 | ISBN: | 9784991191138 | DOI: | 10.23919/ICEP55381.2022.9795638 |
顯示於: | 材料科學與工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。