標題: | Microstructural characterization of Ce-TZP/Al2O3 after degradation in water | 作者: | Tung, Che Lun Cheng, Yung Shin Tien, Chi Shan Hsu, Pei Yi WEI-HSING TUAN Chen, Jin Ren Lai, Po Liang Wu, Ying Ying Shih, Shao Ju Galusek, Dusan |
關鍵字: | degradation resistance | microstructure | phase transformation | Zirconia | 公開日期: | 1-一月-2024 | 卷: | 12 | 期: | 1 | 來源出版物: | Journal of Asian Ceramic Societies | 摘要: | In this study, the long-term resistance of Ce-TZP/Al2O3 specimens to hydrothermal treatment is evaluated in terms of their microstructure. Treatment of the specimens is carried out in an autoclave with water at 134°C for up to 360 h. The biaxial strength and Weibull modulus of the specimens remains unchanged after 120 h of hydrothermal treatment, and their pseudo-plasticity is preserved. However, after 360 h of hydrothermal treatment the biaxial strength decreases by 12% and the Weibull modulus is also decreased. The transformation surface layer is observed through scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The thickness of the transformation layer can be estimated only through TEM analysis, revealing minimal microcrack formation at the surface layer. For comparison, several Y-TZP specimens are also prepared. After 24 h of hydrothermal treatment, the monoclinic phase content in the Y-TZP specimen reached 60%, resulting in a 40% decrease in strength. This strength decrease can be attributed to microcrack formation in the surface layer. |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/640154 | ISSN: | 2187-0764 | DOI: | 10.1080/21870764.2024.2307693 |
顯示於: | 材料科學與工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。