標題: | Application of Optical-fiber Photoreactor for CO2 Photocatalytic Reduction | 作者: | JEFFREY CHI-SHENG WU Wu, Tzu-Hua Chu, Taichi Huang, Hungji Tsai, Dingping |
公開日期: | 2008 | 期: | 47 | 起(迄)頁: | 131-136 | 來源出版物: | Topics in Catalysis | 摘要: | An optical-fiber photoreactor, comprised of 216 xcatalyst-coated fibers, was designed and assembled to transmit and spread light uniformly inside the reactor. The power loss of light transmission inside an optical fiber was calculated using beam propagation method. The optimum length of optical fiber was estimated to be near 11 cm long in order to entirely spread out light energy over surface catalyst. Vapor-phase CO2 was photocatalytically reduced to methanol using the photoreactor under UV irradiation in a steady-state flow system. The solutions of metal-loaded titania were prepared by thermal hydrolysis method. Metal-loaded TiO2 film was coated on optical fibers by dip-coating method. TiO2, Cu/TiO2 and Ag/TiO2 films were uniformly on the fibers and their thicknesses ranged from 27 to 33 nm. The films consisted of very fine spherical particles with diameters of 10-20 nm. The XRD spectra indicated anatase phase for all films. Methanol yield increased with UV irradiative intensity. Maximum methanol rate was 4.12 μmole/g-cat h using 1.0 wt%-Ag/TiO2 catalyst at 1.13 bar of CO2, 0.03 bar of H2O pressures, and 5,000 s mean residence time under 10 W/cm2 UV irradiation. © Springer Science+Business Media, LLC 2008. |
URI: | http://ntur.lib.ntu.edu.tw//handle/246246/93161 http://ntur.lib.ntu.edu.tw/bitstream/246246/93161/1/30.pdf |
DOI: | 10.1007/s11244-007-9022-7 | SDG/關鍵字: | Anatase phase; Dipcoating methods; Light energy; Mean residence time; Optical-fiber photoreactor; Optimum length; Photocatalytic reduction; Photoreactors; Power-losses; Renewable energies; Spherical particle; Steady-state flows; Surface catalysts; Thermal hydrolysis; TiO; Titania; UV irradiation; Vapor Phase; XRD spectra; Carbon dioxide; Catalysts; Fibers; Irradiation; Light; Light transmission; Methanol; Optical fibers; Photocatalysis; Titanium dioxide; Optical films |
顯示於: | 化學工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。