標題: | The effects of coupling bioglass filler content on Bis-GMA-based composite resin 表面偶合生醫玻璃含量對Bis-GMA基底複合材料之影響研究 |
作者: | 林錦吾 張炎林 林峰輝 LIN, CHIN-OWU CHANG, YEN-LIN LIN, FENG- HUEI |
公開日期: | 1994 | 起(迄)頁: | 232-233 | 來源出版物: | 中華民國八十三年度醫學工程科技研討會,(論文集) | 摘要: | Mostd of the inorganec fillers in restorative dental materials were quartz and silicate at the present. Because of their larger hardness than that of denture, abrasing tooth will be happen and polishing difficultly after restoration. On the other side, the weak bonding between resin matrix and fillers cause fillers dropped from the resin, intercrack between interfaces of resin and fillers, materials and cavities. These result in reducing life-time and multipling bacteria in cavities both. Of the investigated materials, coupling bioglass fillers in BIS-GMA based composite resin create chemical bonding at interface, avoid intercrack affected by the differences of thermal expansion, stress cycle and interface potential, also promoting various mechanical properties and considering polishing easily and no aggregate while lifting fillers content. Compotite with either silane treated fillers or not, display better biocompatibility than commercial dental restirative maetrials. And most of the cytotoxicity come from the resin part of the compesite, it also shows the good biocompitibility of bioglass fillers. And we hope all of these will be applied to the field of dental materials in the future.# 0564# |
URI: | http://ntur.lib.ntu.edu.tw//handle/246246/105180 |
顯示於: | 醫學工程學研究所 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。