Composite films of carbon black nanoparticles and sulfonated-polythiophene as flexible counter electrodes for dye-sensitized solar cells
Journal
Journal of Power Sources
Journal Volume
302
Pages
155-163
Date Issued
2016
Author(s)
Li, C.-T.
Lee, C.-T.
Li, S.-R.
Lee, C.-P.
Chiu, I.-T.
Vittal, R.
Wu, N.-L.
Sun, S.-S.
Abstract
A composite film based on carbon black nanoparticles and sulfonated-poly(thiophene-3-[2-(2-methoxyethoxy)ethoxy]-2,5-diyl) (CB-NPs/s-PT) is formed on a flexible titanium foil for the use as the electro-catalytic counter electrode (CE) of dye-sensitized solar cells (DSSCs). The CB-NPs provide the large amount of electro-catalytic active sites for the composite film, and the s-PT polymer serves as a conductive binder to enhance the inter-particle linkage among CB-NPs and to improve the adhesion between the composite film and the flexible substrate. The flexible CB-NPs/s-PT composite film is designed to possess good electro-catalytic ability for I-/I3- redox couple by providing large active sites and rapid reduction kinetic rate constant of I3-. The cell with a CB-NPs/s-PT CE exhibits a good cell efficiency (η) of 9.02 ± 0.01% at 100 mW cm-2, while the cell with a platinum CE shows an η of only 8.36 ± 0.02% under the same conditions. At weak light illuminations (20-80 mW cm-2), a DSSC with CB-NPs/s-PT CE still exhibits η's of 7.20 ± 0.04-9.08 ± 0.02%. The low-cost CB-NPs/s-PT CE not only renders high cell efficiency to its DSSC but also shows a great potential to replace the expensive platinum; moreover it is suitable for large-scale production or for indoor applications.
SDGs
Type
journal article