Fabrication and characterization of chondroitin sulfate-modified chitosan membranes for biomedical applications
Resource
Desalination 234 (1-3): 166-174
Journal
Desalination
Journal Issue
234
Pages
166-174
Date Issued
2008
Date
2008
Author(s)
Abstract
Chitosan (CH) is a biomaterial with antiseptic, bioactive, and biocompatible properties. To further enhance the performance of chitosan membranes, chondroitin sulfate (CS) was utilized to modify the porous chitosan membranes fabricated by the freeze-gelation method. The cross-linking of CS to CH was mediated by ionic interaction and covalent cross-linking using EDC/NHS coupling reagents. The pore structures, mechanical properties, and surface hydrophilicity of the porous chondroitin sulfate-modified chitosan (CH/CS) membranes could be altered by varying the weight ratio of CS to CH. The membranes had interconnected stratiform pore structure with surface pore size ranging from 10 to 40 μm. Among various CH/CS membranes the one with the weight ratio of 90/10 (CH to CS) possessed the highest mechanical strength (18.61 N/g), about 40% increase as compared with the unmodified CH membrane. The addition of CS improved the hydrophilicity of the membranes. Preliminary cell culture experiments revealed that the proliferation of the gingival fibroblasts on the CH/CS surface was slightly better than that on the CH surface. In summary, the CH/CS membranes (especially the 90/10 membrane), due to their higher mechanical strength, hydrophilicity, and better cell compatibility, are promising biomaterials for tissue engineering applications. © 2008.
SDGs
Type
journal article
File(s)![Thumbnail Image]()
Loading...
Name
23.pdf
Size
1.28 MB
Format
Adobe PDF
Checksum
(MD5):5db34fc8a9ba24f74787d5b518bb430b