The effect of steel chemistry on the formation of Fe-Zn intermetallic compounds of galvanneal-coated steel sheets
Journal
Metallurgical and Materials Transactions B
Journal Volume
25
Journal Issue
5
Pages
721-730
Date Issued
1994
Author(s)
Abstract
The effects of steel chemistry on the formation of Fe-Zn intermetallic compounds in the galvanneal coatings have been investigated by examining the microstructure of galvanneal coat-ings on extra-low-carbon (ELC) steel, interstitial-free (IF) steel, and interstitial-free rephos-phorized (IFP) steel. The layer structure of the coatings was revealed by chemical etching. Phases present in each layer were then identified using electron diffraction in transmission elec-tron microscopy (TEM). A two-layer structure, one consisting of the δ phase with a small fraction of the ζ, phase dispersed on the surface and Γ phases and another consisting of the δ and Γ1 phases, was observed in the ELC sample and the IFP sample, respectively. A three-layer structure consisting of the δ, Γ1 + δ, and Γ phases was observed in the IF sample. The presence of C in the steel substrate retarded the alloying between Fe and Zn; while P in the steel favored the formation of the Γ1, phase over the Γ phase by its surface segregation in the steel substrate. The orientation relationship between coating and substrate was also studied by electron diffraction. Three α-Fe/Γ orientation relationships were frequently observed. © 1994 The Minerals, Metals & Material Society.
Type
journal article