The effect of composition change in sol-gel synthesized PSC
Journal
Biomedical Engineering - Applications, Basis and Communications
Journal Volume
20
Journal Issue
1
Pages
53-59
Date Issued
2008
Author(s)
Abstract
Modified calcium silicate cement had previously been developed as a dental retrograde filling. It had great sealing ability, good biocompatibility, and anti-bacterial properties. However, its clinical application was limited by a long setting time and poor handling property. In previous study, 1, 2 the setting property of PSC was greatly improved due the sol-gel process, without the addition of transition metal element. In this study, different ratio of starting material of PSC was prepared. The composition of each group was also altered with the ratio of the starting materials according to the result of XRD pattern. There is no significant difference in pH variation profile between each group. Even though low C 3 S / C 4 AF ratio (DX631 and DX541 groups) possessed high initial strength at first 24 hours after hydration, there was no increase in strength ever since according to the result of microhardness. However, the groups with high C 3 S / C 4 AF ratio (DX811 and DX721 groups) possessed relatively low initial strength at 24 hours after hydration, but the strength increased rapidly and continuously at least for the next six days of hydration. Moreover, the peak intensity of hydration product (Portlandite) on XRD pattern in DX811 group was much higher than other three groups, and this was also in agreement with the result of microhardness. DX811 group is determined to be the optimal one for the further development in the application as root-end filling materials.
Publisher
World Scientific Publishing Co. Pte Ltd
Type
journal article