Coexistence of martensite and strain glass phases in homogenized Ni-rich TiNi shape memory alloys
Journal
Intermetallics
Journal Volume
109
Pages
16-23
Date Issued
2019
Author(s)
Abstract
The transport and thermal properties of homogenized Ti 50-x Ni 50+x shape memory alloys (SMAs) in the range of 1.0 ≤ x ≤ 1.3 (in at. %) by means of electrical resistivity, Seebeck coefficient, thermal conductivity, and heat capacity measurements are presented. From the electrical resistivity measurement, we have observed thermal hysteresis in cooling and subsequent warming curves for x = 1.1 to 1.2 suggesting the occurrence of a martensitic transition. The martensitic transition is also detected in the Seebeck coefficient, thermal conductivity, and heat capacity measurements in these alloys. Despite this, the x = 1.2 alloy shows a negative temperature coefficient of resistivity over the entire temperature range under investigation, indicating the formation of strain glass phase at low temperatures. The existence of the strain glass state is confirmed by the frequency dispersion of the storage modulus measurement. These observations suggest a coexistence of martensite and strain glass phases in a well-controlled composition of the Ti 50-x Ni 50+x system with 1.0 ≤ x ≤ 1.3. It is revealed that the crossover from martensite to strain glass in Ti 50-x Ni 50+x SMAs is mediated via a coexisting of these two phases, which are triggered by a competing interaction between the thermodynamic and kinetic processes at low temperatures.
SDGs
Publisher
Elsevier Ltd
Type
journal article