Preparation of fluorescent tellurium nanowires at room temperature
Resource
Crystal Growth & Design 8 (1): 351-357
Journal
Crystal Growth and Design
Journal Volume
8
Journal Issue
1
Pages
351-357
Date Issued
2008
Author(s)
Abstract
We have demonstrated a simple approach to the synthesis of fluorescent trigonal tellurium (t-Te) nanowires in aqueous solution at room temperature. The t-Te nanowires were prepared from the reduction of tellurium dioxide (TeO 2) with concentrated hydrazine solution through deposition of Te atoms that were reduced from telluride ions (Te2-) and dissolved from amorphous tellurium (a-Te) nanoparticles onto t-Te nanocrystallines. By carefully controlling the growth time from 40 to 120 min, we prepared different sizes of t-Te nanowires; the length changed from 251 to 879 nm, while the diameter only grew from 8 to 19 nm. The absorption wavelength against the diameter of t-Te nanowires displays the diameter dependence of band I (<300 nm). On the other hand, the absorption wavelength against the length of t-Te nanowires displays the length dependence of band II (>600 nm). By increasing the size of t-Te nanowires, their absorption is under a red shift. For example, the maximum wavelengths of the absorption bands for the t-Te nanowires with the lengths of 251 nm are 271 and 602 nm, while those for 879 nm t-Te nanowires are at 280 and 687 nm, respectively. Deconvolution of the photoluminescence profile for t-Te nanowires obtained at 120 min yields four Gaussian peaks centered at 334, 397, 460, and 507 nm. © 2008 American Chemical Society.
SDGs
Type
journal article
File(s)![Thumbnail Image]()
Loading...
Name
86.pdf
Size
1.44 MB
Format
Adobe PDF
Checksum
(MD5):c0bb4e2bb4bc57292a292676c97c602a