Effects of TiC/TiN addition on the microstructure and mechanical properties of ultra-fine grade Ti (C, N)-Ni cermets
Journal
Journal of the European Ceramic Society
Journal Volume
26
Journal Issue
16
Pages
3861-3870
Date Issued
2006
Author(s)
Abstract
Two series of Ti (C, N)-based cermets, one with TiC addition and the other with TiN addition, were fabricated by conventional powder metallurgy technique. The initial powder particle size of the main hard phase components (Ti (C, N), TiC and TiN) was nano/submicron-sized, in order to achieve an ultra-fine grade final microstructure. The TiC and TiN addition can improve the mechanical properties of Ti (C, N)-based cermets to some degree. Ultra-fine grade Ti (C, N)-based cermets present a typical core/rim (black core and grayish rim) as well as a new kind of bright core and grayish rim structure. The average metallic constituent of this bright core is determined to be 62 at% Ti, 25 at% Mo, and 13 at% W by SEM-EDX. The bright core structure is believed to be formed during the solid state sintering stage, as extremely small Ti (C, N)/TiC/TiN particles are completely consumed by surrounding large WC and Mo2C particles. Low carbon activity in the binder phase will result in the formation (Ni2Mo2W)Cx intermetallic phase, and the presence of this phase plays a very important role in determining the mechanical properties of TiN addition cermets. © 2005 Elsevier Ltd. All rights reserved.
Type
journal article