Aging reactions in a 17-4 PH stainless steel
Journal
Materials Chemistry and Physics
Journal Volume
74
Journal Issue
2
Pages
134-142
Date Issued
2002
Author(s)
Abstract
Microstructural development and aging reactions in a commercial 17-4 PH (precipitation hardening) stainless steel have been investigated. It is found that after solution treatment, the steel produces a uniform matrix, which consists chiefly of lath martensite with micro-twins. The age-hardening behavior in the steel studied is similar to that in classical age-hardening alloys. The tempering of martensite has little effect on hardness during aging process in this steel. Transmission electron microscopy (TEM) has revealed the copper precipitates in the specimen aged at 480 °C for 1h, i.e. a peak aging condition. However, at a higher aging temperature, 620 °C, which is much lower than the AC1 temperature, in addition to the formation of copper precipitates, the reformation of austenite has been noticed. The possible reason why the phenomenon of reversed austenite takes place has been discussed. © 2002 Elsevier Science B.V. All rights reserved.
Type
journal article