Efficient inverted solar cells using TiO2 nanotube arrays
Resource
Nanotechnology 19: 255202
Journal
Nanotechnology
Journal Volume
19
Journal Issue
25
Date Issued
2008
Author(s)
Abstract
Using a vertical titania (TiO2) nanotube array, an inverted polymer solar cell was constructed with power conversion efficiency up to 2.71%. In this study, self-organized TiO2 nanotubes arrays were grown by anodizing Ti metal in glycerol electrolyte containing 0.5 wt% NH4F and 1.0 wt% H2O with 20 V potential. The tube length (∼100 nm) was controlled by the thickness of the sputtered titanium layer on the indium–tin oxide (ITO) substrate. The diameter of the tube was approximately 15–25 nm. After annealing in air at 500 °C for 1 h, nanotubes arrays were crystallized to the anatase phase from the initial amorphous state. Following the infiltration of polymeric semiconductor (poly(3-hexylthiophene) and (6,6)-phenyl C60 butyric acid methyl ester, P3HT:PCBM), the filled TiO2 layer had an optical absorption over a range from UV to visible light. The high surface-to-volume ratio of the nanotube arrays structure increased the effective area of the active region. The high efficiency of our solar cell is attributed to the vertical TiO2 nanotube array's enhanced conduction of photo-induced current due to its charge transport capability.
SDGs
Type
journal article
File(s)![Thumbnail Image]()
Loading...
Name
32.pdf
Size
838.14 KB
Format
Adobe PDF
Checksum
(MD5):5e2b7c306b969a93bda5946b06961371