A red-to-gray poly(3-methylthiophene) electrochromic device using a zinc hexacyanoferrate/PEDOT:PSS composite counter electrode
Journal
Electrochimica Acta
Journal Volume
55
Journal Issue
12
Pages
3966-3973
Date Issued
2010
Author(s)
Hong, S.-F.
Abstract
In this paper, we describe a novel red-to-gray poly(3-methylthiophene) (PMeT) electrochromic device (ECD) with the aid of a zinc hexacyanoferrate (ZnHCF)/PEDOT:PSS counter electrode. The application of ZnHCF to an ECD is first reported. ZnHCF has long suffered from poor deposition yield problem, but we demonstrate that a robust ZnHCF film can be prepared by spin coating of a liquid suspension composed of ZnHCF nanoparticles and PEDOT:PSS ink on ITO. It was found that the ZnHCF/PEDOT:PSS composite worked much better with PMeT than pure ZnHCF or pure PEDOT:PSS from both electrochemical and optical aspects. With a LiClO4/PC electrolyte, the PMeT ECD having ZnHCF/PEDOT:PSS as its counter electrode could be reversibly switched between its red state (>0.8 V) and its gray state (<0 V). For a 2 cm × 2 cm prototype device, the response time for coloration was less than 1 s. The maximum transmittance modulation of the device could attain 45.3% at 750 nm, which resulted in a corresponding coloration efficiency of 336.8 cm2/C. The maximum contrast ratio was 5.45 at 720 nm. In addition, the charge capacity of the ECD could retain 95% of its original value after 10,000 cycles of cyclic voltammetry aging test, although an electrodeposited PMeT film alone could be cycled several hundred times only. To sum up, this work proposes a new, cost-effective transparent counter electrode and brings a stable, high visual-contrast PMeT ECD prototype for further development of a red-color bistable display. © 2010 Elsevier Ltd. All rights reserved.
Type
journal article