Effect of silicon in dual phase steel on the alloy reaction in continuous hot-dip galvanizing and galvannealing
Journal
ISIJ International
Journal Volume
54
Journal Issue
10
Pages
2380-2384
Date Issued
2014
Author(s)
Lin, K.-C.
Abstract
The mechanical properties of steels can be significantly improved by alloying with Si. However, Si in dual phase steel retarded the alloy reaction in hot-dip galvanizing and galvannealing; specifically, a continuous Fe–Zn alloy layer was absent on the steel containing 0.44 wt% Si after 25 s of galvannealing at 500°C. This retardation may be due to the Si-rich molten Zn layer, in which the Si resulted from the aluminothermic reduction of Si oxide and the dissolution from the steel substrate.