Preparation and characterization of monodisperse silica nanoparticles via miniemulsion sol�Vgel reaction of tetraethyl orthosilicate
Journal
Journal of Materials Science
Journal Volume
52
Journal Issue
21
Pages
12706-12716
Date Issued
2017
Author(s)
Abstract
Monodisperse silica nanoparticles were prepared via miniemulsion sol–gel reaction of tetraethyl orthosilicate (TEOS). Hexadecane (HD) or hexadecyltrimethoxysilane was used as costabilizer to effectively retard the Ostwald ripening process involved in TEOS miniemulsion. The Ostwald ripening behavior was characterized by dynamic light scattering (DLS), and it was adequately described by the modified Kabal’nov equation. The miniemulsion sol–gel reaction of TEOS/HD with a volume fraction (φc) of 0.024 at 80 °C is stable in the pH range 6–10. By contrast, gelation of reacting miniemulsions occurs at 70 and 100 min at pH 4 and 5, respectively. The weight-average silica particle size (dw) of colloidal products prepared at 80 °C and pH 7 decreases from 59 to 36 nm with low polydispersity index (PDI, in the range 1.02–1.03), determined by transmission electron microscopy, when the φc of HD increases from 0.024 to 0.23. At constant φc (0.024), the resultant silica nanoparticles show larger dw (83 nm) and PDI (1.35) for the TEOS/HD system at pH 10 as compared to the counterpart of pH 7. Furthermore, for the TEOS/HD system at pH 7 and low φc (0.024), dw increases significantly with temperature being increased from 25 to 80 °C. By contrast, the effect of temperature on silica nanoparticle size becomes insignificant when a high level of HD (φc = 0.23) is used. Zeta potential measurements and field emission scanning electron microscopy were used to characterize the surface charge density and morphology of resultant silica nanoparticles.
Publisher
Springer New York LLC
Type
journal article