Growth kinetics of Ag3Sn in silicon solar cells with a sintered Ag metallization layer
Journal
Solar Energy Materials and Solar Cells
Journal Volume
123
Pages
139-143
Date Issued
2014
Author(s)
Abstract
The interfacial reactions and growth kinetics of intermetallic compounds at the solder/sintered Ag metallization interface in silicon solar cells were investigated during solid-state aging. Three common solders (Sn37Pb, Sn36Pb2Ag, and Sn3Ag0.5Cu) were used to conduct several experiments testing the quality of the solder joints in this study. Accelerated tests were performed to determine the long-term reliability of the solder joints. The storage temperatures were 100, 120, 150, and 180±1 C for various aging durations. The results showed that the sintered Ag electrode gradually transformed into an Ag3Sn intermetallic compound (IMC), and the growth kinetics of Ag3Sn remained a diffusion-controlled process during isothermal aging. The formation of Ag 3Sn increased the series resistances (RS) of the cell modules because Ag3Sn had a higher electrical resistivity than sintered Ag did. In addition, the results revealed that Sn3Ag 0.5Cu PV ribbon effectively slowed down the growth kinetics of Ag3Sn. The apparent activation energies for Ag3Sn at Sn37Pb/sintered Ag, Sn36Pb2Ag/sintered Ag, and Sn3Ag0.5Cu/sintered Ag interfaces were calculated to be 104, 108, and 121 KJ/mole, respectively. These kinetics data were established for the first time for the solder alloys commonly used in PV module assembly industry. © 2014 Elsevier B.V.
SDGs
Other Subjects
Accelerated tests; Apparent activation energy; Crystalline silicon solar cells; Diffusion-controlled process; Metallization layers; Series resistances; Solid-state aging; Storage temperatures; Activation energy; Digital storage; Electric resistance; Growth kinetics; Intermetallics; Kinetics; Lead; Metallizing; Photovoltaic cells; Reliability; Silicon solar cells; Silver; Silver alloys; Sintering; Soldering alloys; Tin
Type
journal article