Preparation of Al2O3/Mo nanocomposite powder via chemical route and spray drying
Journal
Journal of Materials Research
Journal Volume
11
Journal Issue
8
Pages
2020-2028
Date Issued
1996
Author(s)
Abstract
A route to prepare nanometer-sized Mo particulates in Al2O3 was attempted by a combination of solution reactions in molecular scale and forcing precipitation by a spray-drying technique. MoO3 was first dissolved in ammonia water and then added in the slurry with high purity, submicrometer Al2O3 powder. Mixed suspension was spray-dried, and then the dried granules were reduced by hydrogen gas and further hot-pressing to a bulky composite at various temperatures. Dissolution of Mo oxide, adsorption reactions on the alumina surface, and surface potential of alumina particles in homogeneous ammonia suspension were studied. Characterization of the granules, including compactability, flowing properties, surface morphology, grain growth of Mo and Al2O3, and mixing homogeneity, were examined. Homogeneity of the spray-dried granules was determined by the calculation of mixing index and the observation of the microstructure of the sintered body. The existence of intergranular, intragranular, and nanosized Mo particulates within Al2O3 grains was observed by transmission electron microscopy (TEM). All the evidence revealed that homogeneous composites with nanometer-sized Mo had been successfully prepared by this attempt with the proposed chemical roue and following the spray-drying process.
SDGs
Type
journal article