Corrosion behaviors of Al-Si-Cu-based filler metals and 6061-T6 brazements
Journal
Journal of Materials Engineering and Performance
Journal Volume
11
Journal Issue
2
Pages
187-193
Date Issued
2002
Author(s)
Abstract
The corrosion behaviors of a series of Al-Si-Cu-based filler metals and the 6061-T6 butt joints brazed with these filler metals are evaluated by polarization tests and immersion tests in a 3.5% NaCl aqueous solution. For comparison, a traditional Al-12Si filler metal is also employed. The results indicate that the Al-Si-Cu-based filler metals before brazing possess much higher corrosion current densities and pitting tendencies than the Al-12Si filler metal. However, brazing of the 6061-T6 alloy with an Al-12Si filler metal produces a wider butt joint, which, in this case, creates a more extensive corrosion region. Severe galvanic corrosion occurs at the 6061-T6 joints when brazed with Al-Si-Cu-based filler metals. However, in the case of the 6061-T6/Al-12Si brazements, selective corrosion of the Al-12Si eutectic phase can be observed. The bonding strengths of the 6061-T6 butt joints brazed with various filler metals are also measured before and after the immersion tests.
Type
journal article