Formation and magnetization reversal mechanisms of nano-size Fe arrays prepared on anodic aluminum oxide templates
Resource
Thin Solid Films, 518(18), 5300-5303
Journal
Thin Solid Films
Pages
5300-5303
Date Issued
2010
Date
2010
Author(s)
Huang, Kai-Tze
Kuo, Po-Cheng
Lin, Ger-Pin
Shen, Chih-Lung
Yao, Yeong-Der
Abstract
Vertically aligned Fe arrays have been self-assembled on anodic aluminum oxide templates by evaporation. The rims of the pores, which act as obstacles to the stacking of atoms, prevent them from forming continuous films. By controlling the Fe nominal thicknesses (τn) from 400 to 5 nm, the morphology is changed from continuous film to isolated arrays, leading to the change of the predominant magnetization reversal from domain wall motion to spin rotation. For samples with τn < 59 nm, isolated, rather than interconnected, morphology is formed. In this range, the coercivity shows a spectacular change for τn = 47 nm, with an array diameter of about 52 nm, achieving a maximum of about 38 kA/m. The critical dimension of single-domain array is therefore determined. The magnetostatic and exchange interactions are reduced due to the thermal fluctuation, and the magnetization leaves from the in-plane direction to be randomly distributed in 3-D, for τn < 27 nm. © 2010 Elsevier B.V.
Type
journal article
File(s)![Thumbnail Image]()
Loading...
Name
316.pdf
Size
23.45 KB
Format
Adobe PDF
Checksum
(MD5):ecc61dc20479b1f8db4b1ee03b3ae8bd