A crosslinked waterborne poly(vinyl acetate) for greenhouse gas fixation with improved elastomeric properties, shape-memory ability, and recyclability
Journal
Journal of Environmental Chemical Engineering
Journal Volume
11
Journal Issue
6
Date Issued
2023-12-01
Author(s)
Chen, Yen Chuan
Huang, Ying Chi
Huang, Yi Hua
Lin, Ying Feng
Huang, Ho Ching
Cheng, Yu Wei
Wu, Chien Hsin
Abstract
The development of raw materials from methane and carbon dioxide holds significant potential to cut greenhouse gas (GHG) emissions and reduce the global carbon footprint. As an important monomer, vinyl acetate (VAc) can be produced by the consumption of acetic acid, which will potentially contribute to the reduction of GHGs emission. However, polymers based on VAc are usually prepared from emulsion polymerization in water which brings about the challenges of using modification processes to improve their properties. Here, a newly developed crosslink was able to establish covalently adaptable networks directly in water, enabling the formation of a poly(vinyl acetate) (PVAc) composite. As a result, PVAc emulsions using a monomer of 100% VAc could be transformed from a soft and weak adhesive polymer into an elastomeric polymer composite network with an elongation (775%) at break and flexibility. With the enhanced rubbery modulus, the polymer possesses characteristics for shape-memory material applications with 93% shape fixity and 99% shape recovery after repeated deformation and shape fixity for three times. The recyclability of the PVAc thermosets was demonstrated after granulating and remolding three times, representing an opportunity for designing a greenhouse gas fixing material.
Subjects
CO fixation 2 | Covalent adaptable networks | Elastomer | Shape memory | Waterborne poly(vinyl acetate)