Solvothermal Preparation and Spectroscopic Characterization of Copper Indium Diselenide Nanorods
Resource
Journal of Physical Chemistry B 110 (35): 17370-17374
Journal
Journal of Physical Chemistry B
Journal Volume
110
Journal Issue
35
Pages
17370-17374
Date Issued
2006
Date
2006
Author(s)
Yang, Yi-Han
Abstract
Single-crystalline chalcopyrite CuInSe(2) nanorods (CuInSe(2)NRs) of 50-100 nm in diameter and up to a few micrometers in length have been synthesized solvothermally. High-resolution transmission electron microscopic images of the CuInSe(2)NRs reveal the d-spacing of 0.335 nm for the (112) crystalline planes and a growth direction along [331]. The near-infrared absorption spectrum of the chalcopyrite CuInSe(2)NRs shows a peak maximum at 1162 nm and an onset at 1262 nm, indicating no apparent blue-shift compared with those of Cu-rich CuInSe(2) thin films. An intense peak at 175.1 cm(-1) in the room-temperature Raman scattering spectrum of CuInSe(2)NRs corresponds to the A(1) phonon mode of tetragonal CuInSe(2) chalcopyrite. The narrower full width at half-maximum (fwhm) of 9.5 cm(-1) for CuInSe(2)NRs, in comparison with fwhm approximately 12 cm(-1) for CuInSe(2) films, indicates a uniform size distribution and single crystallization in the nanorods. Analysis of the photoluminescence from the single-crystalline CuInSe(2)NRs measured at 10 K has categorized the emission into seven groups of transitions as characterized by free excitons, bound excitons, conduction band to acceptor levels, and bound excitons at different defects.
Type
journal article
File(s)![Thumbnail Image]()
Loading...
Name
30.pdf
Size
159.68 KB
Format
Adobe PDF
Checksum
(MD5):083382b4dd13bb501532929d6be2e5bf