Electrochemical and electrochromic properties of novel aromatic poly(amine-amide)s derived from N,N′-bis(4-carboxyphenyl)-N,N′-diphenyl-1,4-phenylenediamine
Journal
European Polymer Journal
Journal Volume
42
Journal Issue
5
Pages
1051-1058
Date Issued
2006
Author(s)
Lin, H.-Y.
Abstract
A series of novel triphenylamine-containing aromatic poly(amine-amide)s were prepared from the dicarboxylic acid, N,N′-bis(4-carboxyphenyl)-N,N′-diphenyl-1,4-phenylenediamine, and various diamines by direct phosphorylation polycondensation. All the poly(amine-amide)s were amorphous, soluble in a variety of organic solvents, and could be solution cast into transparent, tough, and flexible films with good mechanical properties. They had useful levels of thermal stability associated with relatively high glass-transition temperatures (195-280 °C). These polymers exhibited strong UV-Vis absorption bands at 330-346 nm and their photoluminescence showed maximum bands around 516-535 nm in NMP solution. The hole-transporting and electrochromic properties are examined by electrochemical and spectroelectrochemical methods. Cyclic voltammograms of the poly(amine-amide)s prepared by casting polymer solution onto an indium-tin oxide (ITO)-coated glass substrate exhibited two reversible oxidative redox couples at potential 0.73-0.78 V and 1.12-1.18 V, respectively vs Ag/AgCl in acetonitrile solution. All the poly(amine-amide)s exhibited excellent reversibility of electrochromic characteristics by continuous ten cyclic scans between 0.0 and 1.40 V, with a color change from original pale yellowish neutral form to the green and then to blue oxidized forms. © 2005 Elsevier Ltd. All rights reserved.
Type
journal article