https://scholars.lib.ntu.edu.tw/handle/123456789/119622
標題: | 藍光鎂誘鋰外擴散式馬赫任德電光調變器之研製 Fabrication of Mach-Zehnder Electro-Optic Modulator for Blue-Laser Wavelength Using Magnesium-Oxide-Induced Lithium-Outdiffused Waveguide |
作者: | 游朝元 You, Chao-Yuan |
關鍵字: | 鈮酸鋰;馬赫任德;藍光;lithium niobate;mach-zehnder;blue laser | 公開日期: | 2007 | 摘要: | 本文使用鎂誘鋰外擴散法在Z切鈮酸鋰基板上製作操作於藍光波段(473nm)之馬赫任德電光調變器,並與退火式質子交換法進行比較。由實驗結果發現,鎂誘鋰外擴散波導在寬度為3.2μm,氧化鎂厚度為500Å時,以1000°C的溫度擴散30 min可僅導單模態。以此條件製作操作在藍光波段下的馬赫任德電光調變器,在電極長度0.95 cm時,半波電壓為4 V,而訊熄比則約為7dB。對於光折效應的量測結果顯示以鎂誘鋰外擴散式波導製成之電光調變器雖然可正常運作,但其光折效應之影響比傳統的退火式質子交換波導明顯。 In this study, magnesium-oxide-induced lithium-outdiffusion (MILO) method is used to fabricate Mach-Zehnder electro-optic modulators on z-cut lithium niobate substrate for a blue laser source of wavelength 473nm. Similar devices fabricated by traditional annealed-proton-exchanged (APE) method are also prepared for comparison. Experimental data show that an MILO waveguide of width 3.2μm supports only single-mode when it is fabricated by sputtering a MgO thin-film of thickness 500Å and then diffusing at 1000°C for 30 min. Mach-Zehnder electro-optic modulator composed of MILO waveguide for blue-laser wavelength is demonstrated. Its halfwave voltage and extinction ratio are found to be 4.0V and 7dB, respectively, which are better than those fabricated by the APE method. Photorefractive effect on Mach-Zehnder electro-optic modulator is measured. Experimental results show MILO waveguides are found less-resistant to the photorefractive effect, although Mach-Zehnder modulators with MILO waveguides have been successfully fabricated. |
URI: | http://ntur.lib.ntu.edu.tw//handle/246246/50687 | 其他識別: | zh-TW |
顯示於: | 光電工程學研究所 |
檔案 | 描述 | 大小 | 格式 | |
---|---|---|---|---|
ntu-96-R94941018-1.pdf | 23.31 kB | Adobe PDF | 檢視/開啟 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。