Acidity and Catalytic Activity of Phosphoric Acid Modified Titanium Oxide Surface
Resource
Journal of the Chinese Chemical Society 35 (3): 191-198
Journal
Journal of the Chinese Chemical Society
Journal Volume
35
Journal Issue
3
Pages
191-198
Date Issued
1988
Date
1988
Author(s)
李俊徹
Abstract
Abstract By refluxing the anatase form of TiO 2 powder in phosphoric acid, the surface acidity was observed to increase. The amount of acid was determined by n‐butylamine titration in n‐heptane media, and was found to be proportional to the reflux period in phosphoric acid. XRD patterns and IR spectra revealed that the products contained a mixture of the anatase form of TiO 2 and titanium phosphate phases. Based on the calculated acid density on the surface, part of the titrant, n‐butylamine penetrated into the titanium phosphate layers. Further investigations using TGA, FT‐IR and TEM techniques along with surface area measurements indicated that the titanium phosphate phase was coated over the TiO 2 phase. The surface acidity of the phosphoric acid treated anatase increased due to the substitution of Ti‐OH groups by phosphate groups. Nevertheless, the chemical properties of the resultant surfaces were found to be influenced by the internal anatase phase. The kinetic data on the 2‐propanol dehydration reaction, where the activation energies were found to decrease gradually with an increase in phosphate content, also support these conclusion.
SDGs
Type
journal article
File(s)![Thumbnail Image]()
Loading...
Name
02.pdf
Size
350.74 KB
Format
Adobe PDF
Checksum
(MD5):c83c032adc0b7577f1cc59d38125103c