EQUILIBRIUM PHASE-RELATIONS IN THE BI-CA-SR-CU-O SYSTEM AT 850-DEGREES-C AND 900-DEGREES-C
Journal
Journal of Materials Research
Journal Volume
5
Journal Issue
7
Pages
1403-1408
Date Issued
1990
Author(s)
Abstract
The phase relations of equilibrium compounds in the pseudoternary system Bi2O3–(Ca,Sr)O–CuO at 850 and 900°C were studied. The ratio of Ca : Sr was fixed at 1:2. Starting materials of Bi2O3, CaCO3, SrCO3, and CuO with various ratios were mixed, pressed into pellets, and heated at or above and then brought back to 850 or 900°C for different durations to ensure that equilibrium had been reached. The products were cooled in air or quenched in liquid nitrogen and then identified by x-ray powder diffraction. At 850°C, only the superconducting phase, Bi2CaSr2Cu2Ox (2122), was observed inside the triangle. The other stable phases were all positioned on the boundary lines, and included CuO·⅗MO, CuO·MO, CuO·2MO, 1.½Bi2O3·0.9MO, Bi2O3·4MO, Bi2O3·9MO, and a solid solution, Bi2O3·xMO, where 0.16 x 0.82 and MO represents ⅓(CaO·2SrO). At 900°C, the above boundary line phases remained stable but the 2122 phase was not observed. The tie lines among the stable phases in the two isotherms were established.
SDGs
Type
journal article