標題: | Characterization of excitonic features in self-assembled InAs/GaAs quantum dot superlattice structures via surface photovoltage spectroscopy | 作者: | Lee, C. H. Huang, Y. S. Wang, J. S. Chan, C. H. HAO-HSIUNG LIN |
公開日期: | 五月-2007 | 卷: | 101 | 期: | 10 | 起(迄)頁: | 103102 | 來源出版物: | Journal of Applied Physics. | 摘要: | This work systematically investigates the influence of InAs growth conditions and superlattice parameters on the optical properties of InAs/GaAs quantum dot (QD) superlattice structures grown by molecular beam epitaxy. Using surface photovoltage spectroscopy, one directly obtains the absorption spectra up to the highest confined QD levels at room temperature. Based on photoluminescence measurements at different excitation wavelengths, a feature below the fundamental transition is attributed to the transition from uncoupled dots in the bottom layers. The QD transition energy shift was found to be correlated with material intermixing, driven by enhanced strain strength with the increase of layer number and the decrease of spacer thickness, and the growth rate of InAs. A blueshift observed in low growth rate samples is indicative of greatly enhanced intermixing. For QD superlattices grown at a relatively high deposition rate of InAs, the material intermixing effect is gradually enhanced with increasing layer numbers, which will compensate the electronically coupled effect and will prevent further energy shift toward the lower energy side. The absorption wavelengths in 10- and 30-period InAs/GaAs QD superlattices with higher growth rates are near 1.32 μm. The results suggest that these QD superlattice structures can be used as promising active media for long-wavelength QD lasers operating at room temperature. © 2007 American Institute of Physics. |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-34249910614&doi=10.1063%2f1.2733992&partnerID=40&md5=0292ae3aef01e274e9a1c4c5207781d1 | DOI: | 10.1063/1.2733992 | SDG/關鍵字: | Excitons; Molecular beam epitaxy; Photovoltaic effects; Self assembly; Semiconducting gallium arsenide; Semiconductor quantum dots; Spectroscopic analysis; Surface measurement; Excitonic features; Material intermixing; Photoluminescence measurements; Surface photovoltage spectroscopy; Superlattices |
顯示於: | 電機工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。