標題: | Improvement in radiation hardness of oxide by successive irradiation-then-anneal treatments | 作者: | Fu, S.-L. JENN-GWO HWU |
公開日期: | 1989 | 卷: | 32 | 期: | 8 | 起(迄)頁: | 615-621 | 來源出版物: | Solid State Electronics | 摘要: | It was experimentally observed that MOS devices prepared by repeated irradiation-then-anneal treatments were more radiation hard than those without such treatments. A modified isochronal annealing method based on the newly reported flat-band-condition annealing approximation was used in this work to examine the activation energy distribution of the radiation-induced positive charges. It was found that an MOS device after X-ray irradiation with a dose rate of 200 k rads (SiO2)/min for 5 min exhibited a distribution of activation energy ranging from 1.2 to 1.8 eV. A sample which was subjected to a repeated irradiation-then-anneal treatments exhibited a significant reduction in the distribution of activation energy in the low energy region of 1.2-1.5 eV, but not in the high energy region of 1.5-1.8 eV. The activation energy distribution for samples prepared under various postoxidation treatments are discussed. © 1989. |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-0024719143&doi=10.1016%2f0038-1101%2889%2990139-1&partnerID=40&md5=ff9a0e0ab363133f920d0ba3817dc4ba http://scholars.lib.ntu.edu.tw/handle/123456789/347708 |
DOI: | 10.1016/0038-1101(89)90139-1 | SDG/關鍵字: | Heat Treatment--Annealing; Oxides--Radiation Effects; Semiconductor Materials--Radiation Effects; Activation Energy Distribution; Irradiation-Then-Anneal Treatments; Isochronal Annealing; Radiation Hardness; Semiconductor Devices, MOS |
顯示於: | 電機工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。