標題: | All-solution-processed-inverted polymer solar cells on PET substrates with CuOx thin film as an anode interlayer | 作者: | Lin, M.-Y. Lee, C.-Y. Shiu, S.-C. Sun, J.-Y. Lin, Y.-H. Wu, W.-H. Lin, C.-F. CHING-FUH LIN |
公開日期: | 2010 | 起(迄)頁: | 1648-1649 | 來源出版物: | IEEE Photovoltaic Specialists Conference | 摘要: | Low-cost solution process becomes the strategic principle for the fabrication of polymer solar cell. However, the cathode or anode interlayer are usually deposited by using vacuum evaporation due to the hydrophobicity problem and the temperature restriction of PET substrates. Here, we have successfully fabricated copper oxide (CuOx) thin film as an anode interlayer in the inverted P3HT:PC61BM solar cells on the PET substrates at low temperature via the sol-gel method. The CuOx thin film can module the Schottky barrier and form an ohmic contact at the organic/metal interface, which make it a great hole transportation layer. In addition, we post- anneal the devices at 110°C to compensate the defect state at the organic/inorganic interface. Thus, the fill factor of the devices has been increased from 53.3% to 63.5% and the power conversion efficiency of devices has been improved from 3.04% to 3.95%. © 2010 IEEE. |
URI: | http://www.scopus.com/inward/record.url?eid=2-s2.0-78650093740&partnerID=MN8TOARS http://scholars.lib.ntu.edu.tw/handle/123456789/357979 |
DOI: | 10.1109/PVSC.2010.5616556 | SDG/關鍵字: | Defect state; Fill factor; Inverted polymer solar cells; Low temperatures; Low-cost solution; Organic/inorganic interfaces; Organic/metal interfaces; PET substrate; Polymer Solar Cells; Post-anneal; Power conversion efficiencies; Schottky barriers; Sol-gel methods; Solution-processed; Strategic principles; Conversion efficiency; Ohmic contacts; Photovoltaic effects; Schottky barrier diodes; Sol-gel process; Solar cells; Thin films; Vacuum evaporation; Polyethylene terephthalates |
顯示於: | 電機工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。