Infrared brazing of Fe 3Al intermetallic compound using gold-based braze alloy
Journal
Gold Bulletin
Journal Volume
44
Journal Issue
1
Pages
49-56
Date Issued
2011
Author(s)
Abstract
Infrared-brazing Fe 3Al with Au-44Cu as filler metal has been investigated. The brazed joint consists mainly of a β-phase, Au 8-xCu 4+xAl 4, caused by the dissolution of Al from Fe 3Al substrate into the braze alloy. The depletion of Al from Fe 3Al substrate results in the formation of a layer of β-phase particles dispersed in the Fe-rich phase. The highest shear strength for AuCu filler is 327 MPa for specimens infrared brazed at 880°C for 180 s. The brazed joint is mainly fractured along the central β-phase in which the fractograph exhibits quasi-cleavage with dimples. Increasing the brazing time or temperature will deteriorate the bonding strength of the joint, and the fracture mode is prone to cleavage of brittle fracture. Au-44Cu filler demonstrates a great potential for bonding Fe 3Al intermetallic compound. © The Author(s) 2011.
Type
journal article