標題: | Interfacially polymerized thin-film composite polyamide membrane: Positron annihilation spectroscopic study, characterization and pervaporation performance | 作者: | Kao S.-T. Huang S.-H. Liaw D.-J. Chao W.-C. Hu C.-C. Li C.-L. Wang D.-M. Lee K.-R. Lai J.-Y. |
關鍵字: | Interfacial polymerization;PAS;Pervaporation;Polyamide;TFC membrane | 公開日期: | 2010 | 卷: | 42 | 期: | 3 | 起(迄)頁: | 242-248 | 來源出版物: | Polymer Journal | 摘要: | To improve the pervaporation performance of polyamide membrane, thin-film composite (TFC) polyamide membranes were prepared through the interfacial polymerization between m-phenylenediamine (MPDA) or 1,3-phenylenediamine-4- sulfonic acid (MPDASA) and trimesoyl chloride (TMC) on the surface of the modified asymmetric polyacrylonitrile (mPAN) membrane and applied in the pervaporation separation of 70 weight % aqueous isopropanol solutions at 25 ¢XC. The variations in the free volume and the thickness of the active polyamide layer of composite membrane were obtained by positron annihilation spectroscopy (PAS) experiments, in which a variable monoenergy slow-positron beam was used. FTIR-ATR spectroscopy, XPS, scanning electron microscopy, AFM and water contact angle measurements were applied to analyze chemical structures, surface elemental compositions, morphologies, surface roughness and hydrophilicity of the active polyamide layer of composite membrane. From the result of PAS experiments, the S parameter (corresponding to the free volume size and amount) and the thickness of the active polyamide MPDASA-TMC/mPAN layer were found to be lower than those of the active MPDA-TMC/mPAN layer. In the aqueous isopropanol solution dehydration, the MPDASA-TMC/mPAN membrane exhibited a higher permeation rate than but maintained the same water concentration in the permeate as did the MPDA-TMC/mPAN membrane. This is in good agreement with the analysis by PAS. ? The Society of Polymer Science, Japan (SPSJ) All rights reserved. |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/406366 | ISSN: | 00323896 | DOI: | 10.1038/pj.2009.334 |
顯示於: | 化學工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。