標題: | Optical temperature sensing properties of SnO2: Eu3+ microspheres prepared via the microwave assisted solvothermal process | 作者: | Das S. Som S. Yang C.-Y. Lu C.-H. |
關鍵字: | Microsphere;Microwave assisted synthesis;Resolution;Sensitivity;Temperature sensor | 公開日期: | 2018 | 卷: | 97 | 起(迄)頁: | 101-108 | 來源出版物: | Materials Research Bulletin | 摘要: | Eu3+-activated SnO2 hollow microspheres were synthesized via a rapid microwave-assisted-solvothermal route within brief reaction duration of 10 min. The synthesis process was optimized via regulating the microwave power which accelerated the nucleation process along with the elevation of crystal growth. Microscopic analysis revealed the formation of hollow microspheres consisting of tiny SnO2 nanoparticles on the surface. The photoluminescence of SnO2:Eu3+ exhibited a broad band from 400 to 575 nm due to the host and dopant emissions. The emission intensity of SnO2:Eu3+ increased gradually with the increase of the Eu3+ concentration up to 0.75 mol%, and then diminished by the formation of Eu2Sn2O7 phase. The fluorescence intensity ratio (FIR) between the emissions of Eu3+ ions and host were measured by varying temperatures to obtain the sensing performance of materials and the maximum relative-sensitivity was calculated as 1.83% K?1. This research indicated the suitability of SnO2:Eu3+ hollow microspheres for phosphor thermometry. ? 2017 Elsevier Ltd |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/407341 | ISSN: | 00255408 | DOI: | 10.1016/j.materresbull.2017.08.057 |
顯示於: | 化學工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。