標題: | In situ DRIFTS analysis of solid electrolyte interphase of si-based anode with and without fluoroethylene carbonate additive | 作者: | Yohannes Y.B. Lin S.D. Wu N.-L. |
公開日期: | 2017 | 卷: | 164 | 期: | 14 | 起(迄)頁: | A3641-A3648 | 來源出版物: | Journal of the Electrochemical Society | 摘要: | The effect of fluoroethylene carbonate (FEC) additive has been studied in the formation of solid electrolyte interphase (SEI) over Si-based anode using in-situ DRIFTS (diffuse reflectance infrared Fourier transform spectroscopy). SEI species were observed in the first lithiation cycle at an onset potential of 1.4 V in electrolyte containing 2 wt% vinylene carbonate (VC) + 10 wt% FEC and at 1.1 V in electrolyte without FEC additive. With blended VC and FEC, high carbon containing species including poly (FEC), poly (VC), and polycarbonates were identified, while poly (VC) and polycarbonates formed in the absence of FEC. The FEC additive also led to a higher content of organic phosphorous fluorides as compared to the electrolyte containing no FEC. Electrochemical analyses indicated that the combination of 2 wt% VC and 10 wt% FEC resulted in lower impedances and improved the stability of the Si-electrode through cycling as compared to that without FEC. DRIFTS provided evidence that similar SEI species formed after the initiation in the first cycle, and this formation was recorded for five cycles. Finally, possible reactions related to the reductive decomposition of FEC and VC are discussed. ? The Author(s) 2017. Published by ECS. |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/408990 | ISSN: | 00134651 | DOI: | 10.1149/2.0681714jes |
顯示於: | 化學工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。