標題: | Leaching characteristics of solidification system of C3A/CuO | 作者: | Lin C.-F. Huang H.-W. |
公開日期: | 1996 | 出版社: | ASCE - American Society of Civil Engineers | 卷: | 122 | 期: | 4 | 起(迄)頁: | 323-326 | 來源出版物: | Journal of Environmental Engineering | 摘要: | This study was to evaluate the leaching characteristics of a solidification/stabilization system, using a static-renewal leaching test in which the leachant was renewed periodically after intervals of static leaching. Tricalcium aluminate was selected as a solidification agent and CuO as a contaminant to simplify the solidified waste. The model solidified waste matrix was vulnerable to the renewable acetic acid (IN) solutions. The release of Ca was rapid; in about 10 extractions, the amount of Ca released had reached the maximum. Similarly, the leaching of Al was significant; about 90% of the total Al solidified was transferred to the acetic acid solution after 10 extractions. The proton promoted surface reaction is hypothesized to be the controlling process in dissolving the calcium compounds. The dissolution reactions would enlarge the capillary pores and produce new voids in the matrix that enhance solute leaching. Since both Ca and Al hydration compounds were rapidly leached out of the solid matrix, C3A eventually played an insignificant role in immobilizing the CuO constituent. ©ASCE. |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-0030128102&doi=10.1061%2f%28ASCE%290733-9372%281996%29122%3a4%28323%29&partnerID=40&md5=e6b2545e122f5826815146f6869b71af https://scholars.lib.ntu.edu.tw/handle/123456789/409550 |
ISSN: | 7339372 | DOI: | 10.1061/(ASCE)0733-9372(1996)122:4(323) | SDG/關鍵字: | Acetic acid; Calcium compounds; Copper compounds; Dissolution; Hydration; Impurities; Protons; Solidification; Stabilization; Contaminant; Leachant; Solidification agent; Tricalcium aluminate; Leaching |
顯示於: | 化學工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。