https://scholars.lib.ntu.edu.tw/handle/123456789/425098
標題: | The corrosion behaviors of heat-treated SAE 8620 steels | 作者: | Hong, Steven Lin, H. C. YUEH-LIEN LEE Lian, T. S. Tseng, L. Y. Lin, K.M. |
關鍵字: | Corrosion behavior | Heat treatment | Microstructure | SAE 8620 steel | Stress corrosion | 公開日期: | 21-七月-2008 | 卷: | 575-578 PART 2 | 起(迄)頁: | 1190 | 來源出版物: | Materials Science Forum | 摘要: | The corrosion behaviors, including the immersion corrosion, electro-chemical corrosion, stress-corrosion fracture, of heat-treated SAE 8620 steels have been investigated. Experimental results show that the 400°C tempered specimen is only susceptible to local attack of pitting corrosion and can exhibit an excellent corrosion resistance during the static immersion and electro-chemical tests in a 3.5% NaCl solution. The tensile strength and elongation of the normalized and 300-500°C tempered specimens will be reduced when tested in NaCl solutions, especially at a higher testing temperature. The normalized specimen can inhibit effectively the crack-growth under constant loading and the 300-500°C tempered specimens have a sequence of crack-growth rate as 300°C > 400°C > 500°C. |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/425098 | ISSN: | 02555476 | DOI: | https://api.elsevier.com/content/abstract/scopus_id/47249116901 |
顯示於: | 工程科學及海洋工程學系 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。