標題: | Synthesis and characterizations of Ni-NiO nanoparticles on PDDA-modified graphene for oxygen reduction reaction | 作者: | Yung, Tung Yuan Huang, Li Ying Chan, Tzu Yi Wang, Kuan Syun Liu, Ting Yu Chen, Po Tuan CHI-YANG CHAO Liu, Ling Kang |
關鍵字: | Fuel cells | Graphene | Ni | NiO | ORR | PDDA | 公開日期: | 1-一月-2014 | 出版社: | SPRINGEROPEN | 卷: | 9 | 期: | 1 | 來源出版物: | Nanoscale Research Letters | 摘要: | © 2014, Yung et al.; licensee Springer. We are presenting our recent research results about the Ni-NiO nanoparticles on poly-(diallyldimethylammonium chloride)-modified graphene sheet (Ni-NiO/PDDA-G) nanocomposites prepared by the hydrothermal method at 90°C for 24 h. The Ni-NiO nanoparticles on PDDA-modified graphene sheets are measured by transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDS), and selected area electron diffraction (SAED) pattern for exploring the structural evidence to apply in the electrochemical catalysts. The size of Ni-NiO nanoparticles is around 5 nm based on TEM observations. The X-ray diffraction (XRD) results show the Ni in the (012), (110), (110), (200), and (220) crystalline orientations, respectively. Moreover, the crystalline peaks of NiO are found in (111) and (220). The thermal gravimetric analysis (TGA) result represents the loading content of the Ni metal which is about 34.82 wt%. The electron spectroscopy for chemical analysis/X-ray photoelectron spectroscopy (ESCA/XPS) reveals the Ni0 to NiII ratio in metal phase. The electrochemical studies with Ni-NiO/PDDA-G in 0.5 M aqueous H2SO4 were studied for oxygen reduction reaction (ORR). |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/425108 | ISSN: | 19317573 | DOI: | https://api.elsevier.com/content/abstract/scopus_id/84919884394 10.1186/1556-276X-9-444 |
顯示於: | 材料科學與工程學系 |
檔案 | 描述 | 大小 | 格式 | |
---|---|---|---|---|
1556-276X-9-444.pdf | 1.28 MB | Adobe PDF | 檢視/開啟 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。