標題: | Crystallization temperature and activation energy of rf-sputtered near-equiatomic TiNi and Ti50Ni40Cu10 thin films | 作者: | Chen J.Z. JIAN-ZHANG CHEN SHYI-KAAN WU |
公開日期: | 2001 | 卷: | 288 | 期: | 1-3 | 起(迄)頁: | 159-165 | 來源出版物: | Journal of Non-Crystalline Solids | 摘要: | Amorphous thin films of Ti49.93Ni50.07 and Ti49.96Ni40.09Cu9.95 alloys were rf-sputtered onto a (1 0 0) Si-wafer and characterized by X-ray diffraction (XRD), DSC, and Auger electron spectrometer (AES) tests. The amorphous structure of the Ti49.93Ni50.07 films is found to be similar to that of TiXNi1-X rapidly quenched ribbons and mechanically alloyed powders, but more stable than Ti49.96Ni40.09Cu9.95 films, by comparing the wavenumbers (QP) of the broad XRD peaks. The crystalline activation energy, Ea, and the onset crystallization temperature, TX, for a 30¢XC/min DSC heating rate of the Ti49.96Ni40.09Cu9.95 and Ti49.93Ni50.07 films are 388 kJ/mol, 488¢XC, and 416 kJ/mol and 511¢XC, respectively. This also suggests that the amorphous Ti49.96Ni40.09Cu9.95 thin film is less stable than the Ti49.93Ni50.07 film, and can be explained in terms of the enthalpy of mixing. The TX values of amorphous TiXNi1-X materials fabricated by the sputtering technique, by rapid quenching and by mechanical alloying are also compared and discussed. ? 2001 Elsevier Science B.V. All rights reserved. |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/425228 | ISSN: | 00223093 | DOI: | 10.1016/S0022-3093(01)00647-0 |
顯示於: | 應用力學研究所 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。