標題: | Chemical machined thin foils of TiNi shape memory alloy | 作者: | Chen J.Z. JIAN-ZHANG CHEN SHYI-KAAN WU |
公開日期: | 1999 | 卷: | 58 | 期: | 2 | 起(迄)頁: | 162-165 | 來源出版物: | Materials Chemistry and Physics | 摘要: | Ti50Ni50 thin foils up to 10 £gm thickness are successfully fabricated from 100 £gm thickness thin plates using chemical machining. Ultrasonic agitation is applied to enhance the chemical etching process with mixed solutions of HF/HNO3/H2O. The higher the HF/HNO3 volume ratio in the solution, the higher the etching rate and the smoother the surface will be. Thin foils can also be fabricated with the electropolishing process but with a much slower etching rate. Foil thickness by these processes can only be approximately 10 £gm due to the side-etching effect. The martensitic transformation peaks of thin foils shown on the DSC curve are broader for a thinner sample due to the effect of thermal resistance in the DSC sample pans. The enthalpy of transformation also decreases while the foil thickness is reduced due to the effect of the foil surface energy and the energy of plastic deformation. |
URI: | https://scholars.lib.ntu.edu.tw/handle/123456789/425229 | ISSN: | 02540584 | DOI: | 10.1016/S0254-0584(98)00273-9 |
顯示於: | 應用力學研究所 |
在 IR 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。