Title: | Electromechanical properties of embedded multifunctional energy storage composite with activated carbon fiber/PVDF gel electrolyte | Authors: | Chen H.-Y Wu C.-Y Hsueh Y.-T HSUN-YI CHEN HSIN-HAOU HUANG |
Keywords: | Activated carbon; Composite structures; Electrochemical electrodes; Energy storage; Fiber reinforced plastics; Fluorine compounds; Graphite fibers; Solid electrolytes; Supercapacitor; Tensile strength; Tensile stress; Activation procedures; Electrochemical test; Electromechanical property; Gel polymer electrolytes; Glass fiber reinforced composite; Optimal composition; Packaging methods; Specific capacitance; Polyelectrolytes | Issue Date: | 2021 | Journal Volume: | 44 | Journal Issue: | 3 | Start page/Pages: | 252-260 | Source: | Journal of the Chinese Institute of Engineers, Transactions of the Chinese Institute of Engineers,Series A | Abstract: | This paper presents a standardized process for fabricating multifunctional energy storage composites that involves using activated carbon fiber (CF) electrodes and a poly(vinylene fluoride) (PVDF)-based gel polymer electrolyte (GPE) as building materials for embedded supercapacitors. A two-step packaging method was used to fabricate composites that can simultaneously bear mechanical loads and store energy. CF electrodes were subjected to three activation procedures, and the optimal composition of the PVDF-based GPE was determined by comparing the performance of PVDF-based GPEs of various compositions through electrochemical tests. The specific capacitance and energy density of a supercapacitor embedded with a glass-fiber-reinforced composite was 168?mF/g and 140?J/kg, respectively. The aforementioned values were 15.3% and 21.9% higher, respectively, than the corresponding values obtained for a bare cell. Mechanical tests indicated that the average tensile strength of the aforementioned composite was 350.1?MPa. With a gradual increase in the tensile load, the supercapacitor energy density increased by approximately 10% and then plateaued until fracture. Under cyclic tensile loads, the fabricated supercapacitors functioned normally until the composite failed. ? 2021 The Chinese Institute of Engineers. |
URI: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-85103143086&doi=10.1080%2f02533839.2021.1884603&partnerID=40&md5=37f3efee7f0a0d5e8f09acf26f89f9ab https://scholars.lib.ntu.edu.tw/handle/123456789/573122 |
ISSN: | 2533839 | DOI: | 10.1080/02533839.2021.1884603 |
Appears in Collections: | 生物機電工程學系 |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.